Alloy steels are designated by AISI four-digit numbers. They contain different kinds of steels having compositions which exceed the limitations of Mn, C, Mo, Si, Ni, Va, and B set for carbon steels. They are more responsive to the mechanical and heat treatments.
| Element | Content(%) |
|---|---|
| Iron, Fe | 98.07 - 98.67 |
| Manganese, Mn | 0.70 - 0.90 |
| Carbon, C | 0.25 - 0.30 |
| Molybdenum, Mo | 0.20 - 0.30 |
| Silicon, Si | 0.15 - 0.35 |
| Sulfur, S | 0.035 - 0.050 |
| Phosphorous, P | 0.035 |
| Properties | Metric | Imperial |
|---|---|---|
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Hardness, Brinell | 167 - 212 | 167 - 212 |
| Hardness, Knoop (converted from Brinell hardness) | 212 | 212 |
| Hardness, Rockwell B (converted from Brinell hardness) | 91 | 91 |
| Hardness, Rockwell C (converted from Brinell hardness. Value below normal HRC range, for comparison purposes only) | 11 | 11 |
| Hardness, Vickers (converted from Brinell hardness) | 199 | 199 |
| Machinability (annealed and cold drawn. Based on 100 machinability for AISI 1212 steel) | 75 | 75 |
| Production Route | Hot Rolled, Cold Rolled |
|---|---|
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |
ASTM A322
ASTM A331
ASTM A519
SAE J404
SAE J412
SAE J770
1) Structures in Buildings, bridges, railway stations.
2) Fabrication of pipeline components & Industrial equipment.
3) Construction of automotive bodies, warehouses, shipping containers.
4) Commercial appliances, etc.