| Element | Content(%) |
|---|---|
| Iron, Fe | 97.98-98.6 |
| Manganese, Mn | 0.70-0.90 |
| Carbon, C | 0.35-0.40 |
| Silicon, Si | 0.15-0.35 |
| Molybdenum, Mo | 0.20-0.30 |
| Sulfur, S | 0.040 |
| Phosphorous, P | 0.035 |
| Properties | Metric | Imperial |
|---|---|---|
| Elastic modulus | 190-210 GPa | 27557-30458 ksi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
| Hardness, Brinell | 196 | 196 |
| Hardness, Knoop (converted from Brinell hardness) | 218 | 218 |
| Hardness, Rockwell B (converted from Brinell hardness) | 92 | 92 |
| Hardness, Rockwell C (converted from Brinell hardness, value below normal HRC range, for comparison purposes only) | 12 | 12 |
| Hardness, Vickers (converted from Brinell hardness) | 206 | 206 |
| Machinability (annealed and cold drawn, based on 100 machinability for AISI 1212 steel) | 70 | 70 |
Sheets / Plates
| Production Route | Hot Rolled, Cold Rolled |
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |