AISI 1017

Steels having carbon as the major alloying element are called as carbon steels. They contain up to 1.2% manganese and 0.4% silicon. The residual elements such as copper, molybdenum, aluminium, chromium and nickel are also present in these steels. AISI 1017 carbon steel is a medium-low carbon steel, which has good welding property and slightly better machinability, compared to the lower carbon steels. It is soft and can be strengthened during cold working and drawing or forming.

Chemical Composition

Element	Content(%)
Iron , Fe	99.11-99.56
Manganese, Mn	0.30-0.60
Carbon, C	0.14-0.20
Sulfur, S	≤ 0.050
Phosphorous, P	≤ 0.050

Mechanical Properties

Properties	Metric	Imperial
Tensile strength	405 MPa	58700 psi
Yield strength (depending on temper)	340 MPa	49300 psi
Elastic modulus	190-210 Gpa	29700-30458 ksi
Bulk modulus (typical for steel)	140 GPa	27557-30458 ksi
Shear modulus (typical for steel)	80.0 GPa	11600 ksi
Poisson’s ratio	0.27-0.30	0.27-0.30
Elongation at break (in 50 mm)	18%	18%
Reduction of area	40%	40%
Hardness, Brinell	116	116
Hardness, Knoop (converted from Brinell hardness)	135	135
Hardness, Rockwell B (converted from Brinell hardness)	66	66
Hardness, Vickers (converted from Brinell hardness)	120	120
Machinability	65	65

Sheets / Plates

Production Route	Hot Rolled, Cold Rolled
Material Standard	AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry
Size	Width from 100mm to 3000mm ; Length from 500mm to 12000mm
Thickness	0.1mm to 400mm
Delivery Condition	As Rolled, Annealed, Quenched and Tempered, Normalized
Surface Finish	Plain, Brushed, Cladded

AISI 1017 Equivalent Grade / Specifications

ASTM A29

ASTM A576

SAE J1397

JIS S15C

ASTM A510

ASTM A611 (A, B, C, E)

SAE J403

SS 1370

ASTM A513

ASTM A635

SAE J412

ASTM A108

ASTM A519

ASTM A659

AFNOR XC 15

SAE J414

ASTM A544

ASTM A794

AFNOR XC 18

JIS S17C

ASTM A549

ASTM A830

DIN 1.1141

ASTM A575 (M1017)

MIL S-11310 (CS 1017)

JIS S 15 CK

AISI 1017 Applications

1) Structures in Buildings, bridges, railway stations.

2) Fabrication of pipeline components & Industrial equipment.

3) Construction of automotive bodies, warehouses, shipping containers.

4) Commercial appliances, etc.