Carbon steels have carbon as the key alloying element in their composition. They also contain up to 0.4% silicon and 1.2% manganese. In addition, the residual elements such as copper, molybdenum, aluminium, chromium and nickel are present in these steels. AISI 1035 is a water resisting carbon steel whose wear resistance and hardenability are increased by the addition of small quantity of chromium.
| Element | Content(%) |
|---|---|
| Iron, Fe | 98.63-99.09 |
| Manganese, Mn | 0.60-0.90 |
| Carbon, C | 0.310-0.380 |
| Sulfur, S | ≤ 0.050 |
| Phosphorous, P | ≤ 0.040 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength, ultimate | 585 MPa | 84800 psi |
| Tensile strength, yield | 370 MPa | 53700 psi |
| Modulus of elasticity | 190-210 GPa | 29700-30458 ksi |
| Bulk modulus (typical for steel) | 140 GPa | 20300 ksi |
| Shear modulus (typical for steel) | 80 GPa | 11600 ksi |
| Poissons ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 30% | 30% |
| Reduction of area | 53% | 53% |
| Hardness, Brinell | 183 | 183 |
| Hardness, Knoop (converted from Brinell hardness) | 204 | 204 |
| Hardness, Rockwell B (converted from Brinell hardness) | 89 | 89 |
| Hardness, Vickers (converted from Brinell hardness) | 192 | 192 |
| Machinability (based on AISI 1212 steel. as 100 machinability) | 65 | 65 |
| Production Route | Hot Rolled, Cold Rolled |
|---|---|
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |
AMS 5080
ASTM A544 (1035)
MIL S-19434
AFNOR CC 35
B.S. 080 A 37
AMS 5082
ASTM A545 (1035)
MIL S-3289
DIN 1.0501
B.S. 080 M 36
ASTM A29 (1035)
ASTM A546 (1035)
MIL S-46070
UNI C 35
AMS 5080D
ASTM A510 (1035)
ASTM A576 (1035)
QQ S700 (C1035)
SS 1550 AMS 5082A
ASTM A512 (1035)
ASTM A682 (1035)
SAE J1397 (1035)
B.S. 060 A 35
ASTM A108
ASTM A513 (1035)
ASTM A827
SAE J403 (1035)
B.S. 080 A 32
QQ S635
ASTM A519 (1035)
ASTM A830
SAE J412 (1035)
B.S. 080 A 35
1) Structures in Buildings, bridges, railway stations.
2) Fabrication of pipeline components & Industrial equipment.
3) Construction of automotive bodies, warehouses, shipping containers.
4) Commercial appliances, etc.