Grade 310 is a medium carbon austenitic stainless steel, for high temperature applications such as furnace parts and heat treatment equipment. It is used at temperatures up to 1150°C in continuous service, and 1035°C in intermittent service. Grade 310S is a low carbon version of grade 310.
| Element | Content(%) |
|---|---|
| Carbon | 0.08 max |
| Manganese | 2.00 max |
| Silicon | 1.50 max |
| Phosphorus | 0.045 max |
| Sulphur | 0.030 max |
| Chromium | 24.00 - 26.00 |
| Nickel | 19.00 - 22.00 |
| Properties | 310S |
|---|---|
| Grade 0.2 % Proof Stress MPa (min) | 205 |
| Tensile Strength MPa (min) | 520 |
| Elongation % (min) | 40 |
| Hardness (HV) (max) | 225 |
| Production Route | Hot Rolled, Cold Rolled |
|---|---|
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |
1) Structures in Buildings, bridges, railway stations.
2) Fabrication of pipeline components & Industrial equipment.
3) Construction of automotive bodies, warehouses, shipping containers.
4) Commercial appliances, etc.