AISI 317L
Stainless steel grade 317L is a low carbon version of grade 317 stainless steel. It has the same high strength and corrosion resistance as 317 steel but can produce stronger welds due to the low carbon content.
Stainless steel grade 317L is a low carbon version of grade 317 stainless steel. It has the same high strength and corrosion resistance as 317 steel but can produce stronger welds due to the low carbon content.
| Element | Content(%) |
|---|---|
| Iron, Fe | Balance |
| Chromium, Cr | 18-20 |
| Nickel, Ni | 11-15 |
| Molybdenum, Mo | 3-4 |
| Manganese, Mn | 2 |
| Silicon, Si | 1 |
| Phosphorous, P | 0.045 |
| Carbon, C | 0.03 |
| Sulfur, S | 0.03 |
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 595 MPa | 86300 psi |
| Yield strength | 260 MPa | 37700 psi |
| Modulus of elasticity | 200 GPa | 29000 ksi |
| Poisson's ratio | 0.27-0.30 | 0.27-0.30 |
| Elongation at break (in 50 mm) | 55% | 55% |
| Hardness, Rockwell B | 85 | 85 |
| Production Route | Hot Rolled, Cold Rolled |
|---|---|
| Material Standard | AISI, ASTM, ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, IS & Custom Chemistry |
| Size | Width from 100mm to 3000mm ; Length from 500mm to 12000mm |
| Thickness | 0.1mm to 400mm |
| Delivery Condition | As Rolled, Annealed, Quenched and Tempered, Normalized |
| Surface Finish | Plain, Brushed, Cladded |
AISI 317L
ASTM A167
ASTM A182
ASTM A213
ASTM A240
ASTM A249
ASTM A312
ASTM A774
ASTM A778
ASTM A813
ASTM A814
DIN 1.4438
QQ S763
ASME SA240
SAE 30317L
1) Structures in Buildings, bridges, railway stations.
2) Fabrication of pipeline components & Industrial equipment.
3) Construction of automotive bodies, warehouses, shipping containers.
4) Commercial appliances, etc.